Chip interconnect wiring structure with low dielectric constant insulator and methods for fabricating the same

ABSTRACT

A method to achieve a very low effective dielectric constant in high performance back end of the line chip interconnect wiring and the resulting multilayer structure are disclosed. The process involves fabricating the multilayer interconnect wiring structure by methods and materials currently known in the state of the art of semiconductor processing; removing the intralevel dielectric between the adjacent metal features by a suitable etching process; applying a thin passivation coating over the exposed etched structure; annealing the etched structure to remove plasma damage; laminating an insulating cover layer to the top surface of the passivated metal features; optionally depositing an insulating environmental barrier layer on top of the cover layer; etching vias in the environmental barrier layer, cover layer and the thin passivation layer for terminal pad contacts; and completing the device by fabricating terminal input/output pads. The method obviates issues such as processability and thermal stability associated with low dielectric constant materials by avoiding their use. Since air, which has the lowest dielectric constant, is used as the intralevel dielectric the structure created by this method would possess a very low capacitance and hence fast propagation speeds. Such structure is ideally suitable for high density interconnects required in high performance microelectronic device chips.

This application claims priority from Provisional application Ser. No. 60/052,174 which was filed on Jul. 10, 1997.

FIELD OF INVENTION

This invention pertains to the field of microelectronic chip fabrication for logic, memory, communication and microcontroller applications.

BACKGROUND OF INVENTION

The operating speeds of silicon integrated circuits are increasing at phenomenal rates to meet aggressive performance demands in computing, communication and microcontroller applications. This in turn necessitates that the signal propagation delays in the wiring that is used to interconnect the circuits on a chip be reduced so that the performance is not limited or hampered unduly by interconnect delays. Interconnect delays in chips are due to the RC time constants wherein R is the resistance of the on chip wiring and C is the effective capacitance between the signal lines and the surrounding conductors in the multilayer interconnection stack. The resistance of the wiring can be reduced by using a material with a lower specific resistivity than the currently used Al-rich Al—Cu alloys. Copper, which has half the specific resistivity of Al—Cu alloys, is the prime candidate being explored for this purpose. The capacitance of a signal line is a combination of the mutual capacitance between the lines in the same wiring plane (C_(LL)) and between lines in two different levels (C_(CO) or C_(LG)) as shown in FIG. 1, cited from a recent conference (R. Havemann presented at the Proceedings of the 1996 Symposium on VLSI Technology, Honolulu, Hi., Jun. 10, 1996). As shown in the graph associated with this schematic, when feature sizes decrease, the intralevel capacitance C_(LL) becomes the major part of the interconnect capacitance and hence dominates the interconnect delay. Interconnect capacitance can be reduced by reducing the dielectric constant, K, of the insulating medium that surrounds these lines. Hence, there has been a significant effort to identify and use low K insulators in interconnect structures. A whole gamut of insulator materials including fluorinated silica, polymers with and without fluorination, amorphous teflon-like polymers, and aerogels made of porous silica have been proposed as possible low K materials for this purpose.

Progress is being made in fabricating interconnect wiring with copper as the conductor. Since copper, unlike Al, is difficult to pattern by subtractive plasma etching, a “Damascene” process is favored to fabricate copper features embedded in a dielectric medium. One typical version of this process, known as the “dual damascene” process, is described briefly below as an example. After the devices are fully fabricated on a semiconductor wafer, the surface is coated with an ionic barrier such as phosphosilicate glan (PSG), borophosphosilicate glan (BPSG) or silicon nitride and appropriate vias are defined in this barrier by photolithography and etching at locations where contacts for interconnect wiring are required. Subsequently, the etched features are filled with an appropriate conductor such as tungsten.

For the sake of clarity and simplicity, we depict the wafer at this stage of processing as the semiconductor substrate, 10, in FIGS. 2A to 2D and later in FIGS. 4A to 4D. Two layers of dielectrics, 20 and 30, are applied on said semiconductor substrate and patterned by lithography and plasma etching to produce trenches, 50, on the top layer that represent the wiring tracks and vias, 40, in the lower layer that will become the means to connect the wires to the metal level below, as shown in FIG. 2A. Layers 20 and 30 can be made of the same dielectric in which case they can be applied in a single deposition step. In a next step, an electrically conductive barrier/adhesion layer, 60, and a copper-based conductor layer, 70, are deposited on the patterned dielectric structure by one or more of the techniques such as sputtering and/or chemical vapor deposition and electrolytic or electroless plating. This layer has to be thick enough to overfill the vias, 40, and trenches, 50, as shown in FIG. 2B.

The last step is to planarize the top surface by chemical-mechanical polishing (CMP) so that the excess copper and the barrier layer are polished off from the top surface resulting in the inlaid wire/via stack as shown in FIG. 2C. This sequence is repeated several times till the necessary number of wiring layers are built. In a final step, the wafer is coated with an insulating passivation layer, 80, and terminal metal pads, 90, are deposited and connected to the top most wiring level through suitable vias in the passivation layer, 80, as shown in FIG. 2D. These terminal pads are used to assemble the chip on a chip carrier using solder interconnects which enables the chip to communicate with other chips and to send and receive information to the user. Alternate terminal pad processes and structures can also be used in place of the final step described above which enable interconnection using wire bonding, conductive paste bonding and the like. Usually, the wafers are subjected to a 400° C. anneal in a N₂/H₂ mixture to “anneal out” any damage accumulated in the thin gate oxide under the silicon circuit gates due to the various plasma processes used to fabricate the wiring structure.

There are several practical difficulties in integrating the low K dielectric materials in such a wiring structure. First, the physico-chemical properties of many of these low K materials are not optimum for the CMP process. For example, most of the polymer materials are too soft and get eroded at too fast a rate relative to copper during CMP, to allow good control over the inlaid layer thickness. Fluorinated oxide dielectrics are suspected to react with or be prone to wiring methodologies leading to corrosion and adhesion loss. Some of these issues can be contained by applying a hard cap layer over the dielectric to act as a CMP stop layer but this requires additional processing and one has to ensure compatibility of the low K material with the processing of this additional layer. Second, most of the low K polymers degrade under thermal excursions to temperature at or above 400° C. Hence, they are not suitable for the device interconnection application because they cannot withstand the device damage anneal alluded to above. This severely restricts the choice of dielectric which can be used for this purpose. Last, the porous inorganic dielectrics such as aerogels are mechanically weak and friable and are unlikely to withstand the multilayer build process of repeated metal deposition and CMP described above.

Another concern is the penetration of copper into the dielectric materials during the various thermal excursions encountered or the fabrication of the interconnect stack and the final damage anneal step. This can degrade the insulator's dielectric constant and leakage performance and in some cases, facilitate the migration of copper to the device levels during the service life of the chips, leading to device failure. Accordingly, the adhesion/barrier layer described above has to function as a copper diffusion barrier. To achieve this reliably, the adhesion/barrier layer has to be free of defects and rapid diffusion paths such as grain boundaries. This in turn requires conductive barrier films of sizable film thickness. Since the typical conductive barrier films have high electrical resistivity, the presence of a significant thickness of such a film in the conductor cross section leads to an increase in the effective line resistance of the wiring. This is particularly severe for narrow lines typical of advanced chips, where the barrier thickness becomes a significant fraction of the line width itself.

Many of the low K dielectrics are also not compatible with Al—Cu interconnect processing because 400° C. to 450° C. substrate temperatures during deposition and/or post deposition anneals are still required to achieve reliable microstructure and properties of the Al—Cu lines, and repeated excursions to such temperatures (in addition to the final device damage anneal) tend to lead to degradation of many of the low K polymeric insulators, as mentioned earlier.

There are two methods of prior art that claim to address the issues alluded to above.

The first one is a method reported by Jeng et al., (Proceedings of the 1995 International Symposium on VLSI Technology, Systems and Applications, pp. 164-168). Their method is cited pictorially in FIG. 3 from the above referenced publication. These authors propose to fabricate an Al-based wiring level by deposition and subtractive etching; CVD deposition of a low K polymer dielectric (such as Parylene) which conformally coats widely spaced features and fills and planarizes over very narrow spaces between closely spaced lines; plasma or RIE etching of the polymer such that it is nearly removed from the wide spaces while being left intact between the narrow spaces; applying a silicon oxide dielectric overcoat and planarizing the structure; etching the via holes in the oxide layer, depositing metal fill and planarizing; and repeating the sequence to construct the required multilevel interconnect structure.

This method suffers from several limitations. First, the level of conformality versus planarity of the CVD polymer coating is dependent on the feature size and spacing and hence will be pattern dependent within the same wafer. This makes it difficult to ensure definitively what the exact nature of the dielectric medium would be around any given line in an interconnect design. This makes the task of predicting and accounting for interconnect delays in chip designs very difficult. Second, the process is tailored to work with the subtractively patterned Al-based wiring structures and may not be suitable for the dual damascene process (Al or Cu based) since the dielectric layers with trenches or vias are made first and metal is filled in and planarized with the patterned dielectric stack in a subsequent step. This precludes the use of the processing route described in FIG. 3, proposed by Jeng et al., for interconnect structures fabricated by the damascene process.

The second method taught by Chang et al., U.S. Pat. No. 5,559,055, describes a process in which one layer of aluminum-based interconnect wiring, the insulator (silicon dioxide) and a stud layer deposited into the vias in the insulator are first fabricated. A second interconnect wiring layer of Al alloy is then deposited and patterned on top. At this point, the insulator is removed either completely or only from between the metal features by an etching process. The structure is then either fully or partially filled with a lower dielectric constant material. A passivation layer is then deposited over the resulting structure. A net lowering of the dielectric constant is claimed due to the replacement of the oxide material with a lower K insulator with or without trapped voids filled with air.

While this method, in principle, can achieve a uniform and lower effective K value in the structure when the etched gaps are completely filled with a low K dielectric, their structure with partially voided low K dielectric will not yield a uniform or predictable value of effective K. This is due to the fact that the presence or absence of voiding depends in a complex manner on a myriad of factors including the size, spacing and aspect ratio of the metal features and, for solution-based insulator deposition, the viscosity and the solvent content of the filling insulator precursor solution. In an actual microelectronic chip where these feature attributes can vary over a large range in any given metal level this would lead to uncontrolled and unpredictable combination of voided and filled areas making it very difficult to assign an effective dielectric constant. This further complicates the job of designing circuits since the design rules require that the effective dielectric constants be precisely known and be maintained within a narrow range to achieve minimized delay tolerances and hence improved chip performance. Further, Chang et al. teach a method that is restricted to wiring structures based on subtractively etched metal lines (aluminum based) only and do not teach a method to achieve lower effective K in structures made by a damascene process, as described in FIG. 2.

It is an object of the present invention to provide a method to achieve a low K chip interconnect structure made of copper based or Al based alloys by circumventing the problems and limitations described above.

It is another object of this invention to produce a chip interconnection structure that comprises copper or aluminum alloy based interconnect wiring disposed in a low K dielectric (preferably air) predominantly situated as the intralevel dielectric so as to reduce the intralevel capacitance which is the major portion of the interconnect capacitance in closely spaced interconnection wiring.

It is yet another object of the present invention to fabricate these interconnect structures with the readily available set of semiconductor processing tools and materials.

SUMMARY OF THE INVENTION

A broad aspect of the present invention is a low dielectric constant chip interconnect wiring structure and a method to fabricate said structure, including the steps of:

fabricating an integrated circuit (IC) interconnect wiring structure containing one or more wiring and via levels using an aluminum or copper-based conductor material and a suitable organic or inorganic insulator material by using methods well known in the current state of the art such as sputter deposition, plating, chemical vapor deposition (CVD), plasma enhanced CVD (PECVD), and reactive ion etching (RIE) combined with lithographic patterning and chemical-mechanical polishing (CMP);

removing the insulator selectively from all the areas that are not covered over by metallic features, by an etching process such as reactive ion etching, wet chemical etching, electron cyclotron resonance (ECR) down stream etching or laser ablative etching;

applying an optional thin insulating passivation/diffusion barrier material to conformally coat and protect the exposed conductor surfaces;

subjecting the resulting etched structure to any thermal anneal required to remove plasma induced damage to the underlying devices;

attaching a thin free standing sheet of an insulating cover layer to the top surface of the structure;

depositing an optional insulating environmental barrier layer on top of said cover layer;

forming via openings in the environmental barrier layer, cover layer and the thin passivation layer at the sites where connections to I/O terminal pads are required; and

completing the device structure by fabricating the terminal pad metal level.

In a more particular aspect of this invention, the dielectric etch and cover layer attachment are carried out only for the upper most pair of wiring levels while retaining the lower levels of wiring as is with the original high K dielectric in order to simplify the overall process.

BRIEF DESCRIPTION OF THE DRAWINGS

Further objects, features, and advantages of the present invention will become apparent from a consideration of the following detailed description of the invention when read in conjunction with the drawing FIGURES, in which:

FIG. 1 is a schematic cross section of a multilevel chip interconnect structure showing the different capacitive components that contribute to signal delay, with a data plot showing the relationship between feature size and intralevel capacitance C_(LL), inter level capacitance C_(LG) and the total capacitance C_(T).

FIG. 2A shows the cross section of the dual layer dielectric structure with etched vias and trenches for wiring tracks during the fabrication of a multilevel interconnect wiring stack.

FIG. 2B shows the cross section of the structure from FIG. 2A after it has been overfilled with barrier and conducting metal layers.

FIG. 2C shows the cross section of the structure from FIG. 2B after it has been planarized by chemical-mechanical polishing.

FIG. 2D shows the cross section of the finished multilayer stack with its I/O terminal pads.

FIG. 3 is a schematic sketch of the prior art process to achieve embedded low K dielectric structures.

FIG. 4A is a schematic sketch of an interconnect structure produced by damascene polishing process followed by dielectric etch to remove all the dielectric material that is not covered by metal features.

FIG. 4B is a schematic sketch of the structure shown in FIG. 4A after a high temperature forming gas anneal and the deposition of a conformed thin passivation dielectric layer.

FIG. 4C is the schematic sketch of the structure shown in FIG. 4B after laminating a free standing insulating cover layer and applying a thin environmental barrier layer.

FIG. 4D is the schematic sketch of the structure shown in FIG. 4C after terminal vias have been etched and terminal pads are deposited to complete the fabrication of the structure.

FIG. 5 is a scanning electron microscope (SEM) photo of an actual three level trace-via-trace test structure with copper wiring made by the damascene process, said test structure having been plasma etched to remove the polymer dielectric film from between the metal features in the same wiring plane.

FIG. 6 is an SEM photograph of a three level test structure with Al—Cu alloy wiring and oxide dielectric fabricated by a subtractive process, after etching the dielectric material from between the features in the same wiring plane.

FIG. 7 is an SEM cross sectional photograph of a three level structure that has been plasma etched to remove the dielectric between the features in the same level and then coated with a thin conformal silicon nitride passivation layer to protect the metal features.

DETAILED DESCRIPTION

According to a first embodiment of the present invention, a low dielectric constant multilevel wiring structure is created by the following damascene-type sequence:

After the integrated circuit transistors are fully fabricated on a semiconductor wafer, a layer of an insulating ionic barrier such as silicon nitride, PSG or BPSG is applied over these devices and appropriate contact vias are opened in this layer by lithography and RIE. Such a wafer is schematically designated as the semiconductor substrate, 10, in FIGS. 2A through 2D and subsequently in FIGS. 4A through 4D that are used in the following description.

Next, an insulating material such as polyimide Pyralin 2611 or Polyimide 5878 (manufactured by Dupont Inc.) is applied and cured on the semiconductor substrate resulting in layers 20 and 30, to achieve a total thickness required for two interconnect metal levels. Alternately, an inorganic dielectric such as silicon dioxide, silicon nitride or spin-on-glass films can also be used to fabricate these layers. The insulator material making up layers 20 and 30 is chosen for its processability, low internal stress, CMP compatibility and ease of etching by RIE with good selectivity with respect to the metal. Low dielectric constant is not a key requirement for the insulator since it will serve only as the interlevel rather than the intralevel dielectric in the final structure and, hence, has only a secondary effect on the overall interconnect capacitance and delays. Trenches and via holes where the wiring traces are to be located are then formed in the dielectric stack by lithography and RIE. An electrically conductive adhesion/barrier layer (such as Cr, Ta, Ti, W, TiN, TaN, WN, TiSiN or TaSiN or combinations thereof) is applied. The trenches and via are then overfilled with copper deposited by a process such as CVD, sputtering, electroplating, electroless plating, evaporation or combinations thereof. The structure is then planarized by chemical-mechanical polishing (CMP) such that the copper surface is coplanar with the dielectric surface resulting in a dual level metal (DLM) comprising a wiring trace/stud structure in-laid in the dielectric. An optional insulating passivation layer can be applied at this point in order to prevent any reaction between the metal conductor and the next polymer based DLM layer. Additional DLM's are added by the repetition of these process steps as required to complete all levels except the terminal vias and pads that form the upper most patterned level of the wafer.

The wafer is then placed in a plasma etch or a reactive ion etch (RIE) system and etched with a suitable gas mixture, such as one containing freon and oxygen, optimized to remove the polymer from all the areas that are not covered over by metal features with minimal etching of the metal conductor. In effect, the metal lines and studs act as masks and the polymer in the openings between them will be etched away. The resulting structure is schematically shown in FIG. 4A. A scanning electron micrograph of such a structure made by a RIE process is shown in FIG. 5. The structure is robust since the polymer underpins all the fine metal features and holds them in place. Other methods of etching such as wet chemical etching, laser ablation, and plasma etching can also be used to remove the dielectric material from between the metal features. After this etching step, the structure is annealed at an elevated temperature such as 400° C. for a suitable duration to reduce any plasma induced damage in the structure. Depending on the thermal stability and deposition process of the thin passivation layer described in the next paragraph, this anneal step can be performed before or after the application of that passivation coating.

In the next step, a very thin dielectric passivation layer, 100, such as silicon nitride, is deposited as a thin conformal coating as shown in FIG. 4B. The passivation layer covers over all the exposed surfaces and is generally deposited by a PECVD process. This coating, which can be as thin as 5 to 40 nm, will act to seal and passivate all the exposed areas of the lines, vias and dielectric layers and suppress any diffusion or interaction of the metal wiring with the rest of the microelectronics component. This is particularly important since copper can poison silicon devices and adversely affect their transistor characteristics and since absorption of moisture can degrade organic dielectric performance. Alternately, the passivation coating can be a CVD polymer coating such as Parylene that conformally coats the surfaces. Yet another passivation option is to use an electroless or immersion plating of a suitable barrier metal that selectively coats only the exposed metallic feature surfaces of the etched wiring structure.

At this point a thin free standing sheet of insulating material with an adhesive coating on one surface is laminated to the top of the structure to form a taut cover layer, 120, as shown in FIG. 4C. This cover layer can be an insulator with an adhesive coating on one side to allow lamination to the structure and could be made of a material such as polyimide or a photo imageable dielectric. The lamination process is performed preferably in an inert, non-oxidizing environment such as helium, argon or forming gas. An optional environmental barrier layer, 130, such as silicon oxide, silicon nitride or diamond-like carbon can be deposited on top of the cover layer, 120. The function of layer 130 is to prevent ingress of oxygen, moisture and other reactive species that may adversely affect the reliability of the devices and the interconnects. This results in a structure wherein the intralevel dielectric (between the metal features in a given a wiring layer) is air with a K of 1. Vias are then etched into the cover layer, 120, the environmental barrier layer, 130, and the thin passivation coating, 100, at locations where contacts to the input/output terminal pads are required.

In the last step, contact metallurgy for the terminal I/O pads, 90, are deposited and patterned at the proper locations and the wafer fabrication is completed.

FIG. 4D schematically depicts the completed low dielectric constant structure produced by the above method.

According to a second embodiment of the present invention, a low dielectric constant multilevel wiring structure is created by the following sequence:

After the integrated circuit transistors are fully fabricated, a layer of insulating ionic barrier such as silicon nitride, PSG or BPSG is applied over these devices and appropriate contact vias are opened in this layer by lithography and RIE.

Next, a series of blanket films starting with a thin (less than 100 nm thick) adhesion/barrier layer material such as Cr, Ti—W, Ta, TaN, Ti, TiN, W, WN or TiSiN or TaSiN, a 500 to 1000 nm thick layer of Al—Cu or Al—Cu—Si alloy conductor material followed by a thin top layer of the same adhesion/barrier layer material as above are deposited in a single sequence. The stack of films is lithographically patterned into a wiring level using suitable RIE processes known in the state of the art.

Next, an insulator material is coated over the metal features by CVD, PECVD or spin coating and curing processes. The criteria for choosing this insulator are ease of deposition, ease of filling gaps, planarization over feature topography, low stress, ability to withstand any thermal processing needed during structure build and plasma damage annealing (essentially high thermal stability and high glass transition temperature), absence of adverse reactions with the interconnect metal stack and ease of etching with high selectivity relative to the metal stack. Low dielectric constant is not a key requirement for the insulator since it will serve only as the interlevel rather than the intralevel dielectric in the final structure and, hence, has only a secondary effect on the overall interconnect capacitance and delays. The coating is intended to be thick enough to cover all the metallic features and produce a buffer thickness of insulator over the features so that it can be used as the next level insulator. Polymeric materials such as polyimides or inorganic materials such as SiO₂ are ideal candidates for this purpose. The inorganic materials may be more preferable due to their superior thermal stability. An optional planarizing material can be applied and reflowed as needed to achieve a planar topography if not already achieved. Spin on glasses and flowable oxides are typical examples of these planarizing materials which are compatible with the inorganic insulators. Such materials are applied at a minimum thickness required to achieve planarization.

Next, contact via holes are produced at appropriate locations in the insulator overcoat by lithography and RIE to expose metal regions that need to be connected to the next upper level. Another stack of adhesion layer, Al alloy conductor and overcoat metal are deposited on top of this structure. A sintering process is performed at a temperature close to or above 400° C. to reflow the Al alloy layers and to ensure good contact between the two sets of metal stacks deposited separately and to improve the microstructure of the Al alloy film itself. The metal blanket is then etched back by RIE or polished back to be coplanar with the insulator surface. Alternately, the vias can be filled by a selective chemical vapor deposition process that applies a metal such as tungsten to fill the via holes only.

The above sequence of processing is repeated as needed to complete all the wiring levels. At this juncture, the wafer is subjected to reactive ion etching in a plasma comprising, for example, a fluorine containing gas (such as CF₄ or SF₆, for example) and oxygen to etch the dielectric materials not covered by the aluminum alloy lines. Other methods such as wet chemical etching or laser ablation etching can also be employed to accomplish this result. The resulting structure is subjected to any elevated temperature (greater than 400° C.) annealing treatments required to remove plasma damage to the underlying IC devices.

Depending on the thermal stability of the thin passivation layer described in the next paragraph, this anneal step can be performed before or after the application of that passivation coating.

In the next step, an optional dielectric passivation layer such as silicon nitride is deposited as a thin conformal coating over all the exposed surfaces by a process such as, but not limited to, PECVD. This coating which can be as thin as 30 to 40 nm will act to seal the side walls of all the lines and vias and suppress the degradation of the wiring metal and the dielectric during subsequent processing. Alternately, the passivation coating can be a CVD polymer coating such as Parylene that conformally coats the surfaces.

At this point a thin free standing sheet of an insulator with an adhesive coating on one surface is laminated to the top of the structure to form a taut cover layer. This lamination is preferably performed in a He, Ar, forming gas or a similar non-oxidizing ambient.

An optional environmental barrier layer, such as silicon oxide, silicon nitride or diamond-like carbon can be deposited on top of the cover layer. The function of layer is to prevent ingress of oxygen, moisture and other reactive species that may adversely affect the reliability of the devices and the interconnects. This results in a structure wherein the intralevel dielectric (between the metal features in a given a wiring layer) is air with a K of 1. Vias are then etched into the cover layer, the environmental barrier layer and the thin passivation coating at locations where contacts to the input/output terminal pads are required.

In the last step, terminal metal pads are deposited at the above noted via locations to complete the device structure.

In a third embodiment of the present invention, the aluminum alloy wiring can be fabricated by a damascene-type process to achieve the initial multilevel structure. In this case, the following procedure is used to fabricate the low K dielectric-containing final structure:

After the integrated circuit transistors are fully fabricated, a layer of ionic barrier such as silicon nitride, PSG or BPSG is applied over these devices and appropriate contact vias are opened in this layer by lithography and RIE.

Next, a layer of insulating material such as polyimide Pyralin 2611 by Dupont Inc. is spin coated and cured to achieve a total thickness required for two metal/dielectric interconnect levels. The polymer is chosen for its processability, low internal stress upon curing, CMP compatibility and ease of etching by RIE. Alternately, an inorganic dielectric such as SiO₂ deposited by PECVD can also be used since it allows thermal processing to higher temperatures and is more amenable to CMP processing. Low K is not a requirement since this material will only be employed as an interlevel rather than an intralevel dielectric.

The trenches where the wiring traces are to be located and via holes are produced in the dielectric stack by lithography and RIE using state of the art processes (for example, CF₄/oxygen plasma). An adhesion layer metal (such as Ta, Ti, TiN, TaN, TiSiN, W, WN or TaSiN or a combination thereof) is deposited by PECVD, CVD or physical vapor deposition (PVD). This is followed by the deposition of an Al—Cu or Al—Cu—Si alloy needed to overfill the trench/via combination. The structure is then planarized by chemical-mechanical polishing (CMP) such that the metallic surface is coplanar with the dielectric surface resulting in a dual level metal (DLM) wiring/stud structure in-laid in the dielectric. A passivation layer may be applied at this point if subsequent application of insulator is required for further DLM fabrication on top. Additional DLM's are added by the repetition of these process steps as required to complete all levels except the terminal vias and pads that represent the upper most patterned level of the wafer.

The wafer is then etched in a RIE or plasma etch process optimized to etch the dielectric with minimal etching of the metal features to etch back and remove the insulator from all the areas that are not covered over by metal features. In effect, the metal lines and vias act as masks and the polymer in the openings between them will be etched away. The structure is robust since the insulator underpins all the fine metal features and holds them in place. It is annealed at an elevated temperature such as 400° C. for a suitable duration to reduce any plasma induced damage in the structure. Depending on the thermal stability and deposition process of the thin passivation layer described in the next paragraph, this anneal step can be performed before or after the application of that passivation coating.

In the next step, a dielectric passivation layer such as silicon nitride is deposited as a thin conformal coating over all the exposed surfaces by a process such as PECVD. CVD polymer films such as Parylene can also be used for this purpose. Alternately, a metallic passivation/barrier layer that can be deposited by electroless plating or selective CVD to cover only the exposed Al feature surfaces only can also be applied at this stage. The function of this thin passivation/barrier coating which can be as thin as 30 to 40 nm is to seal and protect all exposed areas of the lines and vias and the dielectric layers and suppress any diffusion or interaction of the wiring material with the rest of the device structure.

At this point a thin free standing sheet of an insulator with an adhesive coating on one surface is laminated, preferably in a non-oxidizing ambient, to the top of the structure to form a taut cover layer. An optional environmental barrier layer, such as silicon oxide, silicon nitride or diamond-like carbon can be deposited on top of the cover layer. The function of this layer is to prevent ingress of oxygen, moisture and other reactive species that may adversely affect the reliability of the devices and the interconnects. This results in a structure wherein the intralevel dielectric (between the metal features in a given wiring layer) is air with a K of 1. Vias are then etched into the environmental barrier layer, the cover layer and the thin passivation coating at locations where contacts to the input/output terminal pads are required.

In the last step, terminal metal pads are deposited at the above noted via locations to complete the device structure.

In a fourth embodiment of the present invention, the etching of the insulator and the lamination of the cap layer and the environmental barrier layer as described in the three embodiments above are employed only in the top most plane pair of wiring/stud levels. The benefits in this case are reduced processing cost and potential for higher yield. The performance benefits of the low K material can be harnessed by designing the interconnect layout taking into account the fact that low K air insulator and the attendant capacitance reduction are available at the upper most wiring levels. The intralevel dielectric in the lower wiring levels is predominantly a solid dielectric, by which we mean that is a homogenous solid or a solid material with uniformly distributed micro or nano-sized porosity, such as polymer foams, aerogels or xerogels.

EXAMPLE 1

The etch back approach proposed in the present invention was demonstrated by an experiment using a test wiring structure. This structure comprised an oxidized silicon substrate with a first wiring layer of copper, a second via level of copper and a third wiring level of copper connected to the first level at selected locations by means of said second copper vias. The insulator separating the different levels was Dupont Pyralin 2611 polyimide about 1.2 μm thick. The line widths of the metal features ranged in size from 1 to 4 μm, with spacings ranging from 0.65 to 3.75 μm, and the metal thickness was about 1.2 μm. There was a 100 nm layer of SiO₂ deposited between the layers and on the third polyimide layer to act as CMP and RIE stop layer since these parts were fabricated by the damascene process described above in the first embodiment.

This structure was subjected to RIE to remove the dielectric layers from between the metal features. Typical RIE conditions employed for the polyimide removal were 10 to 30 mTorr of a CF₄/O₂ gas mixture with 80 to 95% oxygen, at an rf power density of 0.25 to 1 Watt/cm². The oxide RIE was carried out in a pure CF₄ gas under similar conditions.

An SEM photograph of the structure after dielectric etching is shown in FIG. 5. It is clear that all the polymer and the oxide layers between both the closely spaced and widely spaced features have been fully removed.

EXAMPLE 2

An oxidized silicon wafer with two wiring levels interconnected at selected location by a via level was the starting point for this experiment. The structure consisted of Al—Cu alloy wiring and via studs and Ti-based or Ta-based adhesion and cap layers approximately 100 nm thick. The dielectric used was PECVD SiO₂ and the build process used to make these substrates was one where the metal lines were fabricated by subtractive patterning followed by overcoating with the oxide dielectric material which was deposited by PECVD process. The features were typically 0.5 to 5 μm in width and spacings in different locations of the wafer.

The wafer was subjected to RIE in CF₄ or CHF₃/O₂ plasma which was 80 to 95% fluorocarbon containing and in the pressure range of 10 to 30 mTorr, at an rf power density of 0.25 to 1 Watt/cm². FIG. 6 is an SEM photograph of the structure after the completion of the etching process. It is evident that the oxide dielectric has been fully removed from the spaces between the aluminum features.

EXAMPLE 3

In an effort to demonstrate the etch back approach followed by conformal coating of a thin passivation dielectric proposed in the present invention, an experiment was performed using a test wiring structure. The structure was identical to the one described in Example 1 comprising wiring trace-via-wiring trace levels with polyimide dielectric between the metal features.

This structure was subjected to RIE to remove the dielectric layers from between the metal features. Typical RIE conditions employed for the polyimide removal were 10 to 30 mTorr of a CF₄/O₂ gas mixture with 80 to 95% oxygen, at an rf power density of 0.25 to 1 Watt/cm². The oxide RIE was carried out in a pure CF₄ gas under similar conditions.

At this point, the wafer was loaded on a grounded substrate holder of a plasma enhanced chemical vapor deposition (PECVD) chamber, and coated with a 20 nm of silicon nitride using a process gas containing 2% silane in helium (30 sccm flow rate) and nitrogen (20 sccm flow rate) and a total pressure of 20 mtorr, radio frequency (rf) power density of about 5 mWatt/cm², and substrate temperature of 260° C.

An SEM photograph of the structure after the deposition of the thin silicon nitride dielectric is shown in FIG. 7. It is estimated that the silicon nitride is about 20 nm thick and has conformally covered the metal features.

EXAMPLE 4

An oxidized silicon wafer with two wiring levels connected at selected locations by a via level was the starting point for this experiment. The structure consisted of Al—Cu alloy wiring and via studs and Ta-based adhesion and cap layers approximately 100 nm thick. The dielectric used was PECVD SiO₂ and the build process used to make these substrates was one where the metal lines were fabricated by subtractive patterning followed by overcoating with the oxide dielectric material which was deposited by PECVD process. The test sites consisted of parallel comb/serpentine wiring within the second wiring level wherein the combs had 1.15 μm widths, the serpentines had 0.7 μm widths and the spaces between the combs and serpentines were 0.7 μm. All wires were 1 μm deep and were up to 1 cm in length. Intralevel capacitance was measured using conventional test electronics (HP 4284A LCR meter) at 10 KHz. In addition to capacitance values, opens and shorts between combs and serpentines were also monitored to ensure that the depassivation process did not interfere with wiring integrity and thereby influence capacitance. Initial capacitance ranged from 9.5 pF to 12 pF depending on the line length of the test site and initial process tolerances.

The wafer was subjected to RIE in CF₄ or CHF₃/O₂ plasma which was 80 to 95% fluorocarbon containing and in the pressure range of 10 to 30 mTorr, and rf power density of 0.25 to 1 Watt/cm. The etched back structure had the typical appearance depicted in FIG. 6 and was again electrically tested. Typical intralevel capacitance values of the same sites ranged from 3.1 to 3.5 pF indicating a factor of 3 to 3.5 drop in the effective dielectric constant at these sites. No new opens and shorts were detected at these sites. Thus, the feasibility of reducing the effective dielectric constant of multilayer interconnect structures by this etch back process is demonstrated.

While the present invention has been described with respect to preferred embodiments, numerous modifications, changes, and improvements will occur to those skilled in the art without departing from the spirit and scope of the invention. 

What is claimed is:
 1. A method in which a multilayer microelectronic interconnect structure is fabricated by applying a double layer thickness of a thermally stable and easily processable first dielectric material on a semiconductor wafer, said first dielectric material having a top layer and a lower layer; patterning and etching trenches for wiring tracks on said top layer and vias in said lower layer of said first dielectric material; depositing a thin electrically conductive barrier/adhesion layer in said trenches and vias and overfilling said trenches and vias with a thick conductive wiring layer metal; planarizing said wiring layer metal by etching or polishing to achieve a coplanar inlaid structure of conductors and vias embedded as metal features in said first dielectric material; repeating the above process until a requisite number of wiring levels in said interconnect structure are fabricated; removing said first dielectric material from all areas of said wafer not directly covered by said conductors by means of an etching process while leaving said first dielectric material intact under said metal features; optionally applying a thin conformal passivation layer to cap and protect the exposed metal features; annealing the etched structure at an elevated temperature in a reducing atmosphere to mitigate any plasma process induced damage; laminating a thin taut insulating cover layer to the top surface of the passivated metal features; optionally depositing a thin insulating environmental barrier layer on top of said cover layer; etching terminal vias in said optional insulating environmental barrier layer, insulating cover layer and said thin conformal passivation layer to provide access for terminal pad contacts; and depositing and patterning terminal metal pads at said via locations to complete said interconnect structure.
 2. A method according to claim 1 in which said etching of said dielectric material is performed only on the top most plane pair of wiring/stud levels of interconnect wiring and the via between them.
 3. A method according to claim 1 wherein said dielectric material is selected from the group comprising polyimides, organic polymers, inorganic polymers, silicon oxide, silicon nitride, spin-on-glass materials or combinations thereof.
 4. A method according to claim 1 where said dielectric material is applied by a process selected from the group comprising spin coating and curing, sputtering, evaporation, chemical vapor deposition or plasma enhanced chemical vapor deposition.
 5. A method according to claim 1 where said dielectric material is patterned by a process selected from the group comprising wet chemical etching, reactive ion etching, plasma etching, plasma assisted etching, electron cyclotron resonance plasma etching, ion beam assisted etching, laser ablation, by direct photolithographic patterning or a combination thereof.
 6. A method according to claim 1 wherein the barrier/adhesion layer material is selected from the group comprising Ta, Ti, Cr, Mo, Nb, W nitrides of these metals, oxynitrides of these metals, silico-nitrides of these metals or a combination thereof.
 7. A method according to claim 1 wherein the conductive wiring layer metal is selected from the group comprising copper, aluminum, copper-based and aluminum-based alloys.
 8. A method according to claim 1 wherein said wiring layer metal is planarized by a process selected from the group comprising reactive ion etching, ion milling, mechanical polishing, chemical-mechanical polishing, electrochemical etching and combinations thereof.
 9. A method according to claim 1 where said dielectric material is etched back by a process selected from the group comprising wet chemical etching, reactive ion etching, plasma etching, plasma assisted etching, electron cyclotron resonance plasma etching, ion beam assisted etching, laser ablation, by direct photolithographic patterning or a combination thereof.
 10. A method according to claim 1 wherein the annealing of the etched structure is done in a reducing environment comprising hydrogen or forming gas which is a mixture containing 2 to 10% hydrogen in nitrogen.
 11. A method according to claim 1 wherein the annealing temperature employed is between 300 and 500° C.
 12. A method according to claim 1 wherein the thin conformal passivation layer is selected from the group of insulators comprising silicon nitride, silicon oxide, silicon oxynitride, polyimides, benzocyclobutene, Parylene or combinations thereof and in the thickness range between 20 and 200 nm.
 13. A method according to claim 1 wherein the thin conformal passivation layer is selectively applied on said conductors only and is selected from the group comprising Ni, Co, Ni—P, Ni—B, Co—P, Co—W—P or alloys thereof and applied in the thickness range of 20 to 200 nm.
 14. A method according to claim 1 wherein the laminated insulating cover layer is a free standing film selected from the group comprising adhesive coated polyimides and photo imageable permanent dielectric materials, with a thickness in the range of 5 to 25 μm.
 15. A method according to claim 1 wherein the environmental barrier layer is selected from the list comprising silicon oxide, silicon nitride and diamond-like carbon or combinations thereof, and with thickness in the range of 50 to 1000 nm.
 16. A method according to claim 1 wherein the terminal vias are produced by reactive ion etching, plasma etching, ion milling, laser ablation or by direct photolithographic patterning of said environmental barrier layer, said laminated cover layer and said thin conformal passivation layer.
 17. A method according to claim 1 wherein said terminal metal pads are wire bond pads, solder pads or TAB bonding pads.
 18. A method in which a multilayer microelectronic interconnect structure is fabricated by depositing blanket layers of a conductive adhesion/diffusion barrier layer material, a highly conducting metal and a conductive barrier material on a microelectronic semiconductor wafer to provide a conducting stack, said wafer having electronic devices formed therein; patterning and etching said conducting stack into a level of interconnect wiring pattern having conductive material features; overcoating said pattern with a thermally stable and easily processable and low stress dielectric coating; etching via holes in said dielectric coating at locations where electrical connection to the next layer above is required; depositing and planarizing a highly conductive material to fill said vias in said dielectric coating; repeating the above steps until a desired number of wiring and via levels are fabricated; etching said dielectric coating from all areas where it is not directly disposed under said conductive material features; optionally applying a coating of a thin insulating passivation layer to protect the exposed surfaces of said conductive material features; annealing said etched structure at an elevated temperature to remove any plasma induced damage to said electronic devices; laminating a thin taut insulating cover layer to the top surface of said passivated conductive material features; optionally depositing a thin insulating environmental barrier layer on top of said cover layer; patterning vias into said environmental barrier layer, said cover layer and said thin passivation layer for terminal pad contacts; and depositing and patterning terminal pads at said patterned via locations to complete the interconnect structure.
 19. A method according to claim 18 in which the etching of said dielectric coating is performed only on the top most plane pair of wiring/stud level of interconnect wiring and the intervening via level.
 20. A method according to claim 18 wherein the conductive adhesion/barrier layer is selected from the group comprising Ti, Ta, Zr, Nb, Cr, Mo, W nitrides of these materials, oxynitrides of these materials, silico-nitrides of these materials and combinations thereof.
 21. A method according to claim 18 wherein the highly conducting material is selected from Al and Al based alloys.
 22. A method according to claim 18 wherein the process for etching the metal stack is selected from the group comprising wet chemical etching, electrochemical etching, reactive ion etching, plasma etching, plasma assisted etching, electron cyclotron resonance plasma etching, ion beam assisted etching, laser ablation, by direct photolithographic patterning or a combination thereof.
 23. A method according to claim 18 wherein said dielectric coating is selected from the group comprising polyimides, silicon oxide, silicon nitride or spin-on-glass materials.
 24. A method according to claim 18 wherein the vias in said dielectric coating are patterned by wet chemical etching, reactive ion etching, plasma etching, laser ablation or by direct photolithographic patterning.
 25. A method according to claim 18 wherein said highly conductive material to fill the vias is selected from the group comprising aluminum, aluminum-based alloys, and tungsten.
 26. A method according to claim 18 wherein said dielectric coating is etched by a process selected from the group of processes comprising wet chemical etching, reactive ion etching, plasma etching, plasma assisted etching, electron cyclotron resonance plasma etching, ion beam assisted etching, laser ablation, by direct photolithographic patterning or a combination thereof.
 27. A method according to claim 18 wherein the annealing of the etched structure is done in a reducing environment comprising hydrogen or forming gas which is a mixture comprising 2 to 10% hydrogen in nitrogen.
 28. A method according to claim 18 wherein the annealing temperature employed is between 300 and 500° C.
 29. A method according to claim 18 wherein the thin passivation cap layer is selected from the group of insulators comprising silicon nitride, silicon oxide, silicon oxynitride, polyimides, benzocydobutene, Parylene, and combinations thereof in the thickness range of 20 to 200 nm.
 30. A method according to claim 18 wherein the thin passivation layer is selectively applied on the conductive material features only and is selected from the group comprising Ni, Co, Ni—P, Ni—B, Co—P, Co—W—P or alloys thereof, applied at a thickness between 20 and 200 nm.
 31. A method according to claim 18 wherein the laminated insulating cover layer is a free standing film selected from the group comprising adhesive coated polyimides and photo imageable permanent organic dielectric materials, with thickness in the range of 5 to 25 μm.
 32. A method according to claim 18 wherein said environmental barrier layer is selected from the group comprising silicon oxide, silicon nitride, Parylene and diamond-like carbon or combinations thereof.
 33. A method according to claim 18 wherein the thickness of said environmental barrier layer is in the range from 50 to 1000 nm.
 34. A method according to claim 18 wherein the vias for terminal pad contacts are produced by reactive ion etching, plasma etching, ion milling, laser ablation or by direct photolithographic patterning of said laminated cover layer and the thin passivation layer.
 35. A method according to claim 18 wherein said terminal metal pads are wire bond pads, solder pads or TAB bonding pads.
 36. A method according to claim 1 further including the application of said thin passivation cap layer first followed by the annealing of the etched and passivated structure at an elevated temperature in a reducing atmosphere to mitigate any plasma induced damage in the devices.
 37. A method according to claim 18 further including the application of said thin passivation cap layer first followed by the annealing of the etched and passivated structure at an elevated temperature in a reducing atmosphere to mitigate any plasma induced damage in said devices.
 38. A method according to claim 36 in which the etching of said dielectric material is performed only on the top most pair of interconnect wiring and the intervening via level.
 39. A method according to claim 37 in which the etching of said dielectric material is performed only on the top most pair of interconnect wiring and the intervening via level. 